Studying the Anticorrosion, Morphological and Adhesion Properties of an Ambient Temperature Cobalt Induced-Phosphate Coating
Author(s):
Abstract:
Different properties of an ambient temperature phosphate coating containing cobalt ions were studied on a steel substrate. Surface treatment on the phosphate coating bath was conducted at T=25 ºC, pH=3.1 and t=30 min. Different analytical techniques including linear polarization, scanning electron microscope (SEM), EDX and Pull off test were employed in order to evaluate the phosphate coating properties. The results obtained from the polarization test revealed that corrosion resistance of the phosphate coating was enhanced in the presence of cobalt ions. SEM micrographs showed a better surface coverage for the cobalt induced phosphate coating. Results obtained from the pull off test also showed that the surface treatment of the steel substrate by phosphate coating reduced adhesion loss of the epoxy coating after 30 days immersion in 3.5 wt% NaCl solution. The decrease in the adhesion loss was more pronounced in the case of using cobalt ions in phosphate coating.
Keywords:
Phosphate coating , Cobalt , Polarization , SEM , Pull off
Language:
Persian
Published:
Journal of Color Science and Technology, Volume:8 Issue: 3, 2014
Page:
221
magiran.com/p1339243
دانلود و مطالعه متن این مقاله با یکی از روشهای زیر امکان پذیر است:
اشتراک شخصی
با عضویت و پرداخت آنلاین حق اشتراک یکساله به مبلغ 1,390,000ريال میتوانید 70 عنوان مطلب دانلود کنید!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی نامحدود همه کاربران به متن مطالب تهیه نمایند!
توجه!
- حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران میشود.
- پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانههای چاپی و دیجیتال را به کاربر نمیدهد.
In order to view content subscription is required
Personal subscription
Subscribe magiran.com for 70 € euros via PayPal and download 70 articles during a year.
Organization subscription
Please contact us to subscribe your university or library for unlimited access!