Effect of Retreatment on the Push-out Bond Strength of MTA-based and Epoxy Resin-based Endodontic Sealers

Background. Further studies on the adhesion properties of MTA-based materials seem necessary due to their growing use in endodontic treatment. This research aimed to assess the effect of retreatment on the bond strength of MTA-based (MTA Fillapex) and epoxy resin-based (AH Plus) sealers.
Methods. ProTaper rotary files were applied to prepare the root canals of 80 human mandibular premolars. Then, the roots were randomly divided intotwo groups of A (n=40) and B (n=40), which were obturated with gutta-percha and MTA Fillapex and AH Plus sealer, respectively. In both groups, the teeth were randomly subdivided into 2 subgroups. No retreatment was carried out in subgroups A1 and B1, while subgroups A2 and B2 were retreated with rotary files and a solvent. Then, a push-out test was performed on four 2-mm slices of each tooth at a distance of 2 mm from the coronal surface after two weeks of incubation. Data were analyzed with two-way ANOVA and statistical significance was set at P Results. Regardless of the procedure followed (P Conclusion. AH Plus sealer exhibited a higher bond strength compared to MTA Fillapex. Retreatment using rotary files and chloroform had no statistically significant effect on the bond strength of sealers evaluated in this study.