Effect of temperature and time, the interlayer on microstructure and mechanical properties of Transient Liquid Phase (TLP) bonding of AISI321 stainless steel
Author(s):
Article Type:
Research/Original Article (دارای رتبه معتبر)
Abstract:
According to the industrys need to an appropriate bonding process for components made of AISI 321 austenitic stainless steel, which is used in power-plant parts such as turbines, transient liquid phase (TLP) bonding of AISI 321 steel using MBF-30 and MBF-20 interlayers was studied in this research. TLP bonding was performed in a vacuum furnace at 1050, 1100 and 1150 oC for 30-120 minutes. The microstructural studies were conducted on the joints using an optical microscope and an scanning electron microscope (SEM). Phase analysis of the joints was also performed a SEM/EDS and XRD system. To investigate the distribution of elements across the joints, line scan analysis was used. The shear strength test and the microhardness measurement test were conducted on the joints, in order to study the joints mechanical properties. The minimum time or complete isothermal solidification at 1050, 1100 and 1150oC was obtained as 75, 45 and 30 minutes, respectively. At the incomplete isothermal solidification condition, Fe-B, Cr-B, Ni-Si and Ni-B phases were observed at the joint centerline and diffusion affected zone (DAZ). With increasing bonding temperature and time, more homogenous joint, lower hardness at the different zones of the joints and higher shear strength were obtained. The maximum shear strength for MBF-30 interlayer was obtained as 99 and 98 percent of that of the base metal, and for MBF-20 interlayer was obtained as 95 and 94 percent of that of the base metal, respectively.
Keywords:
Language:
Persian
Published:
New Materials, Volume:7 Issue: 4, 2017
Pages:
95 to 112
magiran.com/p1770849
دانلود و مطالعه متن این مقاله با یکی از روشهای زیر امکان پذیر است:
اشتراک شخصی
با عضویت و پرداخت آنلاین حق اشتراک یکساله به مبلغ 1,390,000ريال میتوانید 70 عنوان مطلب دانلود کنید!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی نامحدود همه کاربران به متن مطالب تهیه نمایند!
توجه!
- حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران میشود.
- پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانههای چاپی و دیجیتال را به کاربر نمیدهد.
In order to view content subscription is required
Personal subscription
Subscribe magiran.com for 70 € euros via PayPal and download 70 articles during a year.
Organization subscription
Please contact us to subscribe your university or library for unlimited access!