Effect of Different Application Techniques of Universal Bonding System on Microtensile Bond Strength of Bulk-Fill Composites to Primary and Permanent Dentin

This study aimed to determine the microtensile bond strength (μTBS) of a bulk-fill composite to permanent and primary coronal dentin using a universal adhesive in self-etch and total-etch modes.

This in-vitro study was performed on 52 occlusal dentinal surfaces of human primary and permanent teeth. The crowns were cut to the gingival level. The 48 prepared dentin sections were randomly assigned to the following groups (n=13): A: Primary/Total-etch, B: Primary/Self-etch, C: Permanent/Total-etch, and D: Permanent/Self-etch. In groups A and C, after etching for 15 seconds, two layers of a universal bonding (Futurabond U) were applied and cured for 10 seconds. All samples were filled with a bulk-fill composite (x-trafil; VOCO) and cured for 40 seconds. The samples were cut to a bar-shaped dentin block with the dimensions of 1×1×1 mm3, and after 10,000 thermocycles, the μTBS test was accomplished at a crosshead speed of 1 mm/minute. The mean and standard deviation (SD) of μTBS were calculated, and the data were analyzed using two-way analysis of variance (ANOVA) and Fisher's exact test.

The mean μTBS was as follows: A: 15.03±2.0279, B: 11.11±2.4423, C: 23.50±4.8165, and D: 16.26±6.3200 MPa. Futurabond U showed a higher μTBS in the total-etch mode (P<0.001). The permanent teeth had greater μTBS than the primary teeth (P<0.001). Similar percentages of failure modes were observed in the total-etch groups but in the self-etch groups, most failures were in the form of adhesive and mixed.

Greater μTBS was observed in the permanent teeth with