Mechano-chemical activation of MoO3-CuO/C powder mixture to synthesis nano crystalline Mo-Cu alloy
Author(s):
Article Type:
Research/Original Article (دارای رتبه معتبر)
Abstract:
In this study, a high energy planetary ball milling technique was used to synthesize nano-crystalline Mo-Cu alloys. Molybdenum trioxide (MoO3) and copper oxide (CuO) were used as the starting materials. Carbo-thermal co-reduction of mixed Mo and Cu oxides powders was done with milling followed by a heat treatment at a high temperature. Differential thermal analysis/thermogravimetric (DTA/TG) was used to determine the heat treatment temperature of activated powders. X-ray diffraction (XRD) analysis was used to investigate the phase structure during the milling and heat treatment. Field emission scanning electron microscopy (FESEM) has been employed to investigate the morphology of powder particles. It was found that the complete carbo-thermal reduction of the oxides mixture may not be possible by the mechanical milling at the ambient temperature and based on thermodynamic investigations, thermal activation was necessary to reduce a MoO3-CuO mixture to a metallic structure. Some peaks at 400, 600 and 950 °C from DTG results of the mixture sample milled for 10 h were observed which were related to the Cu6Mo5O18, MoO2-Cu and Mo formation during carbo-thermal reduction of the MoO3-CuO mixture, respectively. XRD results showed 10 h milled sample after reduction at 1000 °C contained nano-crystalline Mo-Cu alloys with a mean crystallite size of 42 nm for Mo and 37 nm for Cu calculated by the Scherrer equation
Keywords:
Language:
English
Published:
Journal of Ultrafine Grained and Nanostructured Materials, Volume:51 Issue: 2, Dec 2018
Pages:
153 to 162
magiran.com/p1909887
دانلود و مطالعه متن این مقاله با یکی از روشهای زیر امکان پذیر است:
اشتراک شخصی
با عضویت و پرداخت آنلاین حق اشتراک یکساله به مبلغ 1,390,000ريال میتوانید 70 عنوان مطلب دانلود کنید!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی نامحدود همه کاربران به متن مطالب تهیه نمایند!
توجه!
- حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران میشود.
- پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانههای چاپی و دیجیتال را به کاربر نمیدهد.
In order to view content subscription is required
Personal subscription
Subscribe magiran.com for 70 € euros via PayPal and download 70 articles during a year.
Organization subscription
Please contact us to subscribe your university or library for unlimited access!