In order to improvement of wear resistance of 1.2344 hot work tool steel, Vanadium Carbo-nitride V(N,C) was applied by duplex treatment which involved gas Nitro-carborizing followed by Thermo Reactive Diffusion (TRD) process. The coating layer was investigated by X-Ray diffraction method and SEM microscopy. Hardness profile from surface to the substrate was obtained by Micro-hardness test. Wear rate and coefficient of friction of the V(N,C) coating in comparison with Hardened, Nitrocarborized, and Vanadium carbide (VC) coated samples was evaluated by Pin-on-Disk wear test machine during 700m displacement under 140N normal load. Wear mechanism was investigated by SEM microscopy of wear traces and debris with secondary electron (BSE), back scatter mode, and EDS analyses. Results indicated that duplex process provides a gradual hardness leads to supportive subsurface for the super hard V(N,C) layer. The V(N,C) showed minimum wear rate and friction coefficient due to oxidation of vanadium at high temperature in contact region. The predominant wear mechanism was recognized as a micro-polishing of oxidized layer.Keywords: Duplex coating, Thermo Reactive Diffusion, Wear, Vanadium Nitrocarbide}
بدانید!
- در این صفحه نام مورد نظر در اسامی نویسندگان مقالات جستجو میشود. ممکن است نتایج شامل مطالب نویسندگان هم نام و حتی در رشتههای مختلف باشد.
- همه مقالات ترجمه فارسی یا انگلیسی ندارند پس ممکن است مقالاتی باشند که نام نویسنده مورد نظر شما به صورت معادل فارسی یا انگلیسی آن درج شده باشد. در صفحه جستجوی پیشرفته میتوانید همزمان نام فارسی و انگلیسی نویسنده را درج نمایید.
- در صورتی که میخواهید جستجو را با شرایط متفاوت تکرار کنید به صفحه جستجوی پیشرفته مطالب نشریات مراجعه کنید.