International Journal of iron and steel society of Iran, Volume:16 Issue: 2, Summer and Autumn 2019, PP 29 -33
In the present research, the effect of the homogenization process and annealing temperature were investigated for the 1.4470 ferritic-austenitic stainless steel in the as-cast condition. In this regard, microstructural evolutions, hardness, and impact energy of the steel was evaluated with different heat treatment conditions. The results show that the minimum volume fraction of austenite phase (about 42%) was formed in as-cast condition; while the maximum content of austenite phase can be achieved by annealing at 1010 °C for 45 min. without the homogenizing process (about 56%). Moreover, a good combination of impact energy and hardness was obtained by homogenizing at 1120°C/45 min. and subsequent annealing at 1010°C/15 min. followed by oil quenching. In this condition, the same volume fraction of the ferrite and austenite phase has been formed in the microstructure. and subsequent annealing at 1010°C/15 min. followed by oil quenching. In this condition, the same volume fraction of the ferrite and austenite phase has been formed in the microstructure.
Keywords: Ferritic-austenitic stainless steel, Heat treatment, Microstructure, Mechanical properties}
- در این صفحه نام مورد نظر در اسامی نویسندگان مقالات جستجو میشود. ممکن است نتایج شامل مطالب نویسندگان هم نام و حتی در رشتههای مختلف باشد.
- همه مقالات ترجمه فارسی یا انگلیسی ندارند پس ممکن است مقالاتی باشند که نام نویسنده مورد نظر شما به صورت معادل فارسی یا انگلیسی آن درج شده باشد. در صفحه جستجوی پیشرفته میتوانید همزمان نام فارسی و انگلیسی نویسنده را درج نمایید.
- در صورتی که میخواهید جستجو را با شرایط متفاوت تکرار کنید به صفحه جستجوی پیشرفته مطالب نشریات مراجعه کنید.