جستجوی مقالات مرتبط با کلیدواژه « fe-c-b » در نشریات گروه « مواد و متالورژی »
تکرار جستجوی کلیدواژه «fe-c-b» در نشریات گروه «فنی و مهندسی»-
In the present study, the structural and magnetic characteristics of Fe-Co-Cr system, with 28 at. % of Cr content, during casting, solutioning and thermo-magnetic treatment has been investigated. Based on results, the formation of single α-phase solid solution in the Fe72-xCoxCr28 (10<xThe Co content had negligible effects on magnetic characteristics of Fe62Co10Cr28, Fe60Co12Cr28 and Fe58Co14Cr28 alloys. Fe72-xCoxCr28 (10<x with a constant Cr content of about 28 at. %, were outside the miscibility gap in the equilibrium phase diagram, and therefore TMT had no effect on the final magnetic properties.</x</x
Keywords: Fe-Cr-Co, casting, magnetic properties} -
To probe advantages in Fe-N-SiO2/TiO2 nanocomposite system, the visible photocatalytic degradation of the nonbiodegradable antibiotic oxytetracycline (OTC) by unsupported TiO2 and its modified composites by incorporating each of the Fe, N, and SiO2 dopants under a series of conditions were investigated. The structural and optical properties as well as the morphology of the prepared nanocomposites were also characterized applying Fourier transform infrared (FT-IR), X-ray diffraction, photoluminescence spectroscopy, UV-visible diffuse reflectance spectra and field emission scanning electron microscopy/Energy-dispersive X-ray spectroscopy (FESEM/EDX). In order to develop two models portraying appropriate functional relationships between two main responses (OTC removal efficiency and its specific removal rate (SRR)) and four numerical variables (OTC concentration, catalysis loading, initial pH and reaction time), two separate multivariate analysis pathways under response surface methodology (RSM) were taken. The results obtained all came down to the maximum SRR (220 OTC mg OTC removed/g cat. h) found at the maximum catalyst dosage of 1.5 g/l, and acidic pH of 3 after 0.5 h. Furthermore, the Fe-N-SiO2/TiO2 proved a stable photocatalytic activity during three subsequent reusability experiments, shedding light on its reliable potential for future application.
Keywords: Photocatalytic Degradation, Nonbiodegradable Antibiotics, Fe-N-SiO2, TiO2, Oxytetracycline} -
This study is an attempt to produce surface nanocrystalline composite of Fe-Co-TiO2 at various current densities in the range of 20 to 50 mA/cm2 via pulse electrodeposition method. The prepared composites were characterized by field emission scanning microscope (FESEM), electron dispersive spectrum (EDS), Vickers microhardness, vibrating sample magnetometer (VSM), and x- ray diffraction techniques (XRD). The results showed that the formation of cauliflower morphology was preferred at lower current densities. Moreover, the higher current densities enhanced the Fe content and at the same time diminished the Co and TiO2 contents of prepared surface composites. XRD patterns and Rietveld analysis confirmed the formation of combinations of BCC (as dominant) and FCC phases. Higher current density enhanced the saturation magnetization and decreased lower coercivity due to the higher Fe content and the reduction of TiO2 nanoparticles in coatings. In addition, the lowest coercivity and highest saturation magnetization were gained at 50 mA/cm2, while, the maximum microhardness obtained at 30 mA/cm2.Keywords: Fe based Composite, Pulse electrodeposition, Soft Magnetic Properties, Vickers Microhardness}
-
در این تحقیق اثر افزودن نیترات آهن به عنوان پیش ماده کاتالیستی جهت تشکیل درجای نانو ذرات Fe در رزین های فنولیک و تاثیر آن بر ریزساختار دیرگدازهای MgO-C بررسی شده است. بدین ترتیب جهت بررسی ریزساختار و سیستم اتصالی دیرگداز، رزین های بدون افزودنی و حاوی افزودنی به فاز زمینه دیرگداز MgO-C افزوده شد. نمونه های آماده شده در دماهای ºC800، ºC1000، ºC1200 و ºC1400 در اتمسفر احیایی پخت شد و جهت بررسی فازهای تشکیل شده در زمینه دیرگداز و بررسی های ریزساختاری از XRD و FESEM استفاده شد. در این تحقیق درصد آهن نسبت به رزین 0 و 6 درصد وزنی انتخاب شد. نتایج نشان داد نیترات آهن در طول فرآیند پخت در اتمسفر احیایی تبدیل به نانو ذرات آهن با اندازه متوسط 60 تا nm80 می شود. تشکیل درجای نانو ذرات آهن و تاثیر کاتالیستی آن، منجر به گرافیته شدن کربن حاصل از پیرولیز رزین فنولیک از دمای ºC800 شد و با افزایش دما نانو لوله های کربنی توخالی و بامبو شکل و کربن پوست پیازی در ریزساختار تشکیل و بر مقدار آن ها افزوده شد. از طرفی با حضور نانو ذرات آهن، سرعت انجام برخی واکنش های ریزساختار در فاز زمینه دیرگداز در حین فرآیند پخت بهبود یافت و مورفولوژی فازهای تشکیل شده در ریزساختار بعد از فرآیند پخت به مقدار قابل توجهی از حالت ذره ای به الیافی تغییر کرد. نتایج حاصل از بررسی های ریزساختاری نشان داد الیاف Al4C3 و AlN از دمای ºC1000 تشکیل شده و با افزایش دما به ºC1200 الیاف رشد و مقدار آن ها نیز افزایش یافت. همچنین در دمای ºC1200 الیاف MgAl2O4 و MgO نیز تشکیل شد که با افزایش دما به ºC1400 تراکم آن ها به مقدار قابل توجهی افزایش یافت. حضور نانو ذرات Fe در نمونه ها باعث قوی تر شدن نقش آنتی اکسیدان Al در تشکیل فازهای سرامیکی شد. مشاهدات ریزساختاری نشان داد عمدتا الیاف سرامیکی در فاز اتصالی و بین اگریگیت ها تشکیل می شوند و فرآیند تشکیل الیاف و نانو لوله های کربنی تشکیل شده غالبا از طریق دو سازوکار بخار-مایع-جامد (V-L-S) و بخار-جامد (V-S) بوده است.
کلید واژگان: نانو ذرات آهن, کاتالیست, نانو لوله های کربنی, الیاف سرامیکی}In the present study, the effect of Iron Nitrate as catalytic precursor to in situ formation of nano-Fe particles in phenolic resin and microstructural evolution of MgO-C refractories has been investigated. Therefore, various samples according to matrix section formulation of low carbon MgO-C refractories (LCMCR’s) with 0 and 6 wt% (Fe/Phenolic resin) were prepared and phase and microstructure changes after coking at temperatures 800-1400ºC studied by XRD and FESEM analyses. Based on attained results, iron nitrate transfer to Fe nano particles with 60-80 nm in diameter during firing in reduced atmosphere. In situ formed Fe nano-particles as catalytic agent promotes graphitization behavior of phenolic resins. Increasing temperature led to a more effective graphitization level. In addition, the different nano crystalline carbon shapes such as onion and bamboo like and carbon nanotubes (CNTs) were in situ formed. Phase and microstructure analysis of LCMCR’s samples reveal that different ceramic whiskers such as MgO, MgAl2O4 spinel, Al4C3 and AlN formed after coking at 1000 ºC and the amount of whiskers phases significantly increased at higher coking temperatures. It was also clarified the presence of Fe nano-particles have effective influence on the formation of gases components and promote ceramic phases formation. Microstructural observation showed the graphitic carbons like carbon nano-tubes (CNTs) and ceramic whiskers mainly formed in the bonding phase between the aggregates according to the V-L-S and V-S growth mechanism.
Keywords: Fe nano particles, Catalyst, CNTs, Ceramic whiskers} -
The application of hardfacing materials for producing wear-resistant coatings on components working in wear conditions is one of the important advices in environmental protection and increasing the service life of engineering equipment. In this study, the microstructure of the hardfaced layers made by two cored wires containing Fe-B and Fe-B-C powder-based were investigated. ST37 plain carbon steel was used as the substrate and the deposition of the hardfaced layers was conducted by the flux cored arc welding (FCAW) process under single-, two-, and three-pass conditions. The microstructural and phase analyses were carried out by field emission scanning electron microscopy (FE-SEM) and X-ray diffraction (XRD), respectively. The results showed that the characteristic microstructures of the Fe-B hardfacing alloy layers comprised a matrix containing elliptical dendritic ferrite and the eutectic of (α-Fe2B). But, the Fe-B-C hardfacing alloy layers included columnar-like Fe2B, skeletal-like Fe2B, daisy like Fe3(C, B) and the eutectic of (P-Fe2B).Keywords: Hardfacing, Microstructure, Fe-B, Fe-B-C, FCAW}
-
در این تحقیق، با استفاده از دو سیم جوش مغزه دار حاوی پودر پایه Fe-B و Fe-B-C، عملیات روکش کاری سخت بر روی فولاد st37 به روش FCAW (جوشکاری قوسی توپودری) ، طی سه فرایند تک پاسی، دو پاسی و سه پاسی انجام پذیرفت. نتایج نشان داد با افزایش تعداد پاس در هر دو سیم جوش، درصد بور منطقه جوش نیز از 3/2 تا 18/3 درصد وزنی افزایش می یابد که این امر را می توان به دلیل حضور بیشتر بور در مذاب جوش به دلیل افزایش حجم سیم جوش در هر پاس از فرایند جوشکاری دانست. همچنین بررسی های ریزساختاری نشان داد با استفاده از سیم جوش Fe-B فرایند جوشکاری تک پاسی منجر به ایجاد زمینه فریت و یوتکتیک ? -Fe2B می گردد که در فرایند دو پاسی نسبت به فرایند تک پاسی جزایر فریتی کمتر شده و در عوض میزان یوتکتیک ? -Fe2B افزایش می یابد. فرایند جوشکاری پاس سوم منجر به ایجاد ذرات اولیه Fe2B ستونی شکل و یوتکتیک ? -Fe2B می گردد. حضور کربن در سیم جوش Fe-B-C باعث تشکیل جزایر پرلیتی در کنار ذرات اولیه Fe2B خواهد شد. همچنین در پاس سوم جوشکاری با هر دو سیم جوش، مقادیر بسیار کمی فاز FeB در اطراف فاز Fe2B اولیه تشکیل می شود. حضور ترکیب FeB را نیز می توان به دلیل جدایش عنصر بور در جوشکاری در طی انجماد غیر تعادلی دانست. نیز افزایش سختی بدست آمده را می توان به دلیل افزایش بور در اثر افزایش تعداد پاس های جوشکاری دانستکلید واژگان: جوشکاری قوسی توپودری, روکش کاری سخت, Fe, B, ریزساختار, پاس جوشکاری}In present investigation, hard claddings treatment was performed on st37 steel using two cored electrodes containing Fe-B and Fe-B-C powder-based by FCAW (Flux Cored Arc Welding) method during three stages of single pass, two-pass and three-pass welding process. Results indicated that the increasing of welding pass numbers for both welding electrode, boron percentage was improved from 2.3 to 3.18 wt. % at weld metal due to more presence of boron in liquid phase which caused volume increase of electrode at each welding pass. Microstructure observation results also expressed that the using of Fe-B electrode for single pass welding process caused to create a ferrite matrix and α-Fe2B eutectic; for two-pass welding process compared to single pass ferrite islands have been decreased, while the amount of α-Fe2B eutectic have been increased. Third pass of welding process caused to form α-Fe2B eutectic and primary particles of Fe2B which had columnar shape. Presence of carbon in Fe-B-C electrode will form pearlite islands beside primary Fe2B. Also, at third pass of welding process by both electrodes, very low amount of FeB phase would be formed around the Fe2B primary phase. Formation of FeB compound related to segregation of boron element during welding and non-equilibrium solidification. The increase in hardness can also be attributed to an increase in the amount of boron due to the increasing number of welding passesKeywords: flux, cored Arc welding, hardfacing, Fe, B, microstructure, welding passes}
-
امروزه سنسورهای گازی به طور گسترده برای کنترل اتمسفر محیط مورد استفاده قرار می گیرند. در این پژوهش، لایه نازک PEDOT:PSS/Fe(salen) تهیه شده به روش پوشش دهی چرخشی، به عنوان حسگر گاز منواکسید کربن مورد استفاده قرار گرفت. کامپوزیت حاصل، با استفاده از روش های مختلف ازجمله طیف سنجی نوری( UV-Vis) و طیف سنجی تبدیل فوریه مادون قرمز( FT-IR) مشخصه یابی شد. همچنین، توپوگرافی سطح کامپوزیت لایه نازک با استفاده از میکروسکوپ نیروی اتمی ( AFM ) مورد بررسی قرار گرفت. این کامپوزیت روی بسترهای شیشه ای با الکترودهای شانه ای درهم فرورفته پوشش داده شد. الکترود حاصل هنگام قرار گیری در معرض گاز CO در شرایط معمولی اتاق (20RH=%) و با کاهش فوری مقاومت مواجه شد. نتایج نشان داد که پاسخدهی سنسور موردنظر یک طرفه نیست و با حذف گاز CO از محفظه دوباره به مقاومت اولیه خود برمی گردد (RD< 2%). بالاترین فاکتور پاسخدهی و کمترین زمان پاسخدهی (t90) بدست آمده به ترتیب برابر با 77/0%±40 و 38 ثانیه می باشند. در نهایت، مقدار بهینه ی ترکیب برای کامپوزیت ساخته شده، (02/0 درصد وزنی Fe(II)(salen))) تعیین گردید.کلید واژگان: سنسور شیمیایی, Fe(II)(salen), PEDOT:PSS, لایه نازک, منواکسید کربن}Gas sensors are now widely used for routine monitoring of the quality of atmospheres. A sensitive PEDOT:PSS/Fe(salen) thin film based toxic gas sensor deposited on glass pieces with interdigitated Au electrodes was developed by the spin coating method. The obtained composite was well characterized by different techniques such as UVvis spectroscopy and FTIR. Also, the surface topography of thin film composite was investigated using AFM. The Fe(salen)-doped PEDOT:PSS on interdigitated electrode was experienced an immediate decrease in resistance when exposed to carbon monoxide gas under normal dry room temperature conditions (%RH=20). The results showed that the response of desired sensor was not unidirectional, and reverses to the original resistance level when CO was removed from the test chamber (RDKeywords: Chemical sensor, Fe(II)(salen), PEDOT:PSS, Thin film, Carbon monoxide}
-
In the present research, thixoforming route was carried out in order to enhance the microstructural features of LM28 piston alloy. Typical microstructure of this alloy was composed of coarse, polygonal primary silicon particles, eutectic matrix and intermetallic phases. Thermal analysis was carried out to study the solidification path of the base alloy and determine the major arrest temperatures of metallurgical reactions. Continuous and iso-thermal mechanical stirring were utilized to produce non-dendritic LM28 alloy feedstock for further processing. The rheocast samples were subjected to a rotation speed of 450 rpm. The slugs machined from the solidified rheocast specimens were heated in the mushy zone temperature and then were thixoformed via a laboratory press. The thixoformed specimens show a relatively homogenous microstructure and present no evidence of porosities. Fine, blocky primary silicon and Fe-rich intermetallic particles were uniformly distributed in the matrix of LM28 alloy. Optical microscope and scanning electron microscope linked with EDX were used to investigate the microstructure of specimensKeywords: Piston Alloy, Thermal Analysis, Thixoforming, Primary Silicon, Fe-Rich Intermetallic}
-
آرایه های نانوسیمی Fe100−x Mn x (0 ≤ x ≤ 87) با استفاده از الکتروانباشت همزمان Fe و Mn در حفرات قالب اکسید آلومینیوم آندی (AAO) ساخته شده در آزمایشگاه سنتز شدند. تاثیر ترکیب درصد فلزات انباشت شده، دمای تابکاری و فرکانس الکتروانباشت بر ساختار بلوری و خواص مغناطیسی نانوسیم های سنتز شده مورد بررسی قرار گرفت. تغییرات مغناطش اشباع، وادارندگی (Hc) و نسبت مربعی (Mr/Ms) و تغییر ساختار بلوری با تغییر پارامترهای فوق مطالعه گردید. نتایج تصاویر SEM وطیف XRD ساختار bbc نانوسیم ها را مشخص نموده و نشان می دهد که فاز بلوری با تغییر دمای تابکاری تغییر می نماید. نانوسیم های تشکیل شده دارای ناهمسانگردی مغناطیسی تک محوره با جهت مغناطیسی آسان در امتداد محور نانوسیم می باشند که ناشی از ناهمسانگردی شکلی بزرگ است. همچنین، وادارندگی نانوسیم های Fe100−x Mn x با افزایش دمای تابکاری برای همه ترکیبات افزایش می یابد. از سوی دیگر، نانوسیم های الکتروانباشت شده در فرکانس های مختلف رفتار مغناطیسی متفاوتی را نشان می دهند زیرا با افزایش فرکانس الکتروانباشت سرعت احیا یونهای فلزی در قالب کاهش می یابد.کلید واژگان: نانوسیم, الکتروانباشت, وادارندگی, آلیاژ آهن-منگنز}Ordered Fe100−x Mn x (0 ≤ x ≤ 87) nanowire arrays have been prepared by co-electrodeposition of Fe and Mn into pores of homemade anodized aluminum oxide (AAO). The influence of composition, annealing temperature, and frequency on structure and magnetic properties of Fe/Mn nanowires was studied. The changes in the saturation magnetization, coercivity (Hc), remanent squareness (Mr/Ms), and crystal structure of nanowires with changing of the above parameters were also investigated. The results of XRD and SEM suggest that the nanowires have a bcc structure and that their phases change with the annealing temperature. The nanowires have uniaxial magnetic anisotropy with easy magnetization direction along the nanowire axis due to the large shape anisotropy. Also, the coercivity of the Fe100−xMn x nanowires was increased with increasing annealing temperature for all the compositions. On the other hand, the nanowire arrays electrodeposited at different electrodeposition frequencies show remarkably different magnetic behaviors, due to increasing of the electrodeposition frequency, the rate of ions for reduction was decreased.Keywords: Nanowire, Electrodeposition, Coercivity, Fe-Mn alloy}
-
در این پژوهش، عملکرد فتوکاتالیستی پودرهای کامپوزیتی نانوساختار Fe-39 %FeS سنتز شده به روش مکانوترمال مورد بررسی قرار گرفت. ابتدا مخلوط پودری Fe و S با نسبت اتمی آهن به گوگرد برابر 1:2 تحت فعال سازی مکانیکی قرار گرفت و سپس به مدت دو ساعت در دمای 850 درجه سانتی گراد عملیات حرارتی شد. به منظور مشخصه یابی پودر سنتز شده از آنالیزهای پراش پرتو ایکس (XRD)، میکروسکوپ الکترونی روبشی گسیل میدانی (FESEM) و طیف سنج مرئی – فرابنفش (UV-vis spectroscopy) بهره برده شد. نتایج XRD سنتز موفق ساختار کامپوزیتی Fe-FeS را نشان داد. تصاویر FESEM نیز ذرات پودری با اندازه کمتر از دو میکرون را پس از عملیات حرارتی نمایش می دهد. هم چنین در بررسی فتوکاتالیستی، تاثیر pH به عنوان عامل موثر بررسی شد. نتایج نشان داد که در محیط های بازی میزان تخریب متیلن بلو بیشتر از محیط های اسیدی و خنثی است که در مورد pH برابر 11 پس از تابش 195 دقیقه نور مرئی 91 درصد از متیلن بلو مورد تخریب قرار گرفت. علاوه بر این نتایج بررسی های سینتیکی نیز نشان داد که فرآیند تخریب فتوکاتالیستی در ابتدا (75-0 دقیقه) از مدل درجه اول پیروی ولی با گذشت زمان با تغییر سازوکار از مدل درجه دوم پیروی می کند.کلید واژگان: فتوکاتالیست, کامپوزیت, نانوساختار, Fe, FeS, سینتیک, PH}In this paper, photocatalytic activity of mechanothermally synthesized Fe-39%FeS nanostructured composite powder is investigated. Fe and S powders mixture with atomic ratio of 2:1 (Fe:S) is mechanically activated and then heat treated at 850?C for 2 h. X-ray diffraction (XRD), Field Emission Scanning Electron Microscopy (FESEM) and UV-vis spectroscopy are applied for characterization of composite powder. XRD results are shown that Fe-FeS powder was synthesized successfully. FESEM images showed that powder with the size of less than 2 ?m is formed after heat treatment. Also, the effect of pH as an effective factor is investigated. It can be seen that the degradation efficiency in basic solution is higher than acidic and neutral solution. Dyes degradation reached to 91% after 195 min irradiation of visible light in pH=11. In addition, kinetic study showed that the photocatalytic dedradation is initially (0-75 min) followedKeywords: Photocatalyst, Composite, Nanostructure, Fe, FeS, Kinetics, pH}
-
Ilmenite, aluminum and graphite can be used to produce in-situ Al2O3/TiCFe composites which are used as cutting tools. Few publications can be found in the literature that discusse the effect of molar ratio of aluminum and graphite on the Al2O3/TiCFe formation mechanism. Therefore, the present research is designed to make the issue clear. To achieve this goal, at first, the mechanism of the Fe-TiC/Al2O3 composite formation from ilmenite, aluminum and graphite mixture with molar ratio of 1:2:1 was clarified. Then the samples with different molar ratios of aluminum and graphite were prepared. Both of aluminum and graphite ratios changed separately in this work. In the following, the samples were heat treated at 1300°C to be sure all reactions are completed. It was found that the optimum molar ratio of ilmenite, aluminum and graphite mixture is 1:2:1 because no undesired compound was detected in the products. Compared with the ratio of 1:2:1, increasing the aluminum content of the raw materials causes the TiAl3 formation while insufficient aluminum doesnt allow the reactions to be completed. It also was found that using more graphite leads to form the Fe-C compounds and less graphite will cause the reaction not to be completed.Keywords: Ilmenite, Aluminum, Graphite, Fe, TiC, Al2O3 composites, molar ratio}
-
در این پژوهش بس لایه های Co-Cu/Cu و Fe-Co-Cu/Cu بر روی زیر لایه شیشه /طلا به روش الکتروانباشت لایه نشانی گردید. ناهمواری های سطحی این لایه ها به وسیله میکروسکوپ نیروی اتمی بررسی شده و سپس با رسم نمودار ناهمواری سطحی بر حسب طول اسکن در مقیاس لگاریتمی نوع و اندازه ناهمواری های سطحی مورد محاسبه قرار گرفت. ساختار بس لایه ها توسط پراش اشعه ایکس مورد مطالعه قرار گرفت و پیک های مشخصه و ساختار بلوری لایه ها بدست آمد. رابطه بین ضخامت لایه های مغناطیسی و میزان درصد جرمی کبالت انباشت شده در هر دو بس لایه توسط آنالیز تفکیک انرژی پرتو ایکس بررسی شد. پس از آن اندازه و شکل دانه ها و رابطه آن با ضخامت و مواد سازنده بس لایه ها در هر یک از بس لایه های مغناطیسی توسط میکروسکوپ الکترونی روبشی بررسی گردید. در نهایت خواص مغناطیسی بس لایه ها و منحنی پسماند آن ها در حالت موازی بر سطح مورد مطالعه قرار گرفت.کلید واژگان: الکتروانباشت, بس لایه, Co, Cu, Cu, Fe, Co, Cu, Cu}In this research Co-Cu/Cu and Fe-Co-Cu/Cu multilayer were electrodeposited on sputtered gold on glass substrates. The kinetic roughening of samples was investigated by atomic force microscopy (AFM) images and the logarithmic scale plots of roughness as a function of scan lengths. The XRD patterns indicate the multilayer thin films follow their substrate textures. The EDX results show that in both Co-Cu/Cu and Fe-Co-Cu/Cu multilayers the Co content increases as the magnetic layer thickness increasing. The SEM images show that increasing the magnetic and nonmagnetic layers thicknesses leads to increase the grain size of multilayers. The Magnetic property studies of samples reveal that the coercivity decreases and the remanence increases by presenting of Fe in magnetic multilayers.Keywords: Electrodeposition, Multilayer, Co-Cu, Cu, Fe-Co-Cu, Cu}
-
آمونیوم پرکلرات بعنوان یک اکسیدکننده قوی، کاربرد بسیار زیادی در فرمولاسیون پیروتکنیک و پیشرانه دارد. براساس استادارد نطامی برخورداری از خلوص بالا و عاری از ناخالصی هایی نظیر کلرات که می توانند بر کارایی آن تاثیر گذار باشند، از اهمیت بالایی برخوردار می باشد. بنابراین حذف ناخالصی ها در فرآیند تولید آمونیوم پرکلرات بسیار مورد توجه خواهد بود. در این مقاله، حذف کلرات با استفاده از فرآیند احیایی با استفاده از نانوذرات فلزی مورد تحقیق قرار گرفت. در این کار، ابتدا نانو ذرات دوفلزی آهن – نیکل پایدار شده تهیه گردید و به منظور مشخصه یابی آنها، آنالیزهای FE-SEM، EDS و XRD انجام گردید. نانو ذرات با اندازه ذرا ت حدود 50-20 نانو متر بدست آمدند. نانو ذرات تهیه شده جهت حذف انتخابی کلرات در آمونیم پرکلرات در محیط آبی به کار برده شد. فاکتور های اصلی که فرآیند حذف را تحت تاثیر قرار می دهند مانند pH ، دمای واکنش، زمان انجام واکنش ومقدار نانو ذارت بررسی شد و مقادیر بهینه آنها نیز مشخص گردید. در شرایط بهینه برای حذف 50 میلی لیتر محلول حاوی کلرات و پرکلرات با نسبت مولی1 به 50، حذف 100 درصدی کلرات مشاهده گردید. روش پیشنهادی برای حذف کلرات در محلول اشباع آمونیوم پرکلرات که در فرآیند تولید مورد استفاده قرار گرفته می شود، نتایج رضایت بخشی را نشان داد.کلید واژگان: آمونیوم پرکلرات, کلرات, نانو ذرات دوفلزی, حذف انتخابی}Ammonium perchlorate is widely used as an oxidizer in the propellant formulation and pyrotechnics According to military standard having high purity and free of impurities such as chlorate . So, the removal of impurities in the production of ammonium perchlorate will be highly regarded. In this paper, the removal of chlorate was investigated by reducing process using metal nanoparticles. In this work, at first, stabilized Ni/Fe bimetallic nanoparticles (S-Ni/Fe NPs) was synthesized and the structure and size of the particles were investigated by XRD, FE-SEM, and EDS. Nano particles were obtained with particle size of 20-50 nm. Prepared nanoparticles were used for the selective removal of chlorate in aqueous ammonium perchlorate. The main factors that affect the removal process such as pH, reaction temperature, reaction time and amount of nanoparticles were investigated and the optimum values were determined. Chlorate in the presence of perchlorate showed a removal of 100 percent, while the perchlorate had been removed to a very small amount.The proposed method for the removal of chlorate in a saturated solution of ammonium perchlorate, which is used in the production process, was showed satisfactory results.Keywords: Ammonium perchlorate, Chlorate, Selective removal, Stabilized- Ni, Fe bimetallic nanoparticles}
-
In this investigate, plain carbon steel cladded by SMAW in single, two and three- pass with two hardface electrodes containing molybdenum, tungsten, and vanadium. Scanning electron microscopy, X-ray diffraction, wear tests and microhardness test were carried out to evaluate the microstructure and wear properties of hardface layers. The results indicated that by increasing of molybdenum concentration in hardface layer, M6C and M7C3 carbides were appeared in the microstructure. Moreover, by increasing the number of hardfaced layers and reducing dilution, the concentration of alloying elements, and the carbides coarser increased at microstructure. Also by increasing the percentage of the molybdenum the hardness of layers increased up to the 61 HRC and 1540 Vickers at the three-pass. In addition by increasing the number of passes the wear resistance of the hardfaced layers increased.Keywords: Hardfacing, SMAW, complex carbide, Fe-C-Cr}
-
In this research, Fe-C-B hardfacing layer fabricated with cored wire contains ferroboron on mild steel by FCAW process. OES, ICP, XRD, OM, SEM, and microhardness method were used for study of characteristics of hardface layer. The chemical analysis test results show that boron was absorbed in hardface layer. The XRD, OM, SEM, EDS results, shows that the microstructure consisted of primary Fe2B, FeB and eutectic structure (A+M+Fe2B) in hardface layer. The hardness test (HRC) results show that hardness of hardface layer was increased than that the base metal. The wear test results shows, in dry (ASTM G65) and wet (ASTM G105) conditions, the Fe-C-B hardface layer has higher wear resistance than that the mild steel and the wet wear resistance of the Fe-C-B hardface is higher than that the dry conditions. In addition, SEM observation of worn surfaces indicated that the wear micromechanism of hardface samples in dry condition was microploughing with cutting, but in the wet condition, was microploughing with pittingKeywords: Fe-C-B, Hardfacing, FCAW, Mild Steel, Abrasive Wear}
-
International Journal of iron and steel society of Iran, Volume:13 Issue: 2, Summer and Autumn 2016, PP 1 -6Transformation induced plasticity (TRIP) steels have a vast application in automotive industry because of their high strength, high ductility and hence excellent energy absorption capacity. These characteristics of TRIP steels are due to the existence of retained austenite in their microstructures in the ambient temperature, which transforms to the martensite phase during deformation. The microstructure of TRIP steel contains various phases and in the past-published studies mainly the volume fraction of retained austenite was investigated and there is not a quantitative comprehensive investigation about all phases in the microstructure of this steel. The main goal in this study is a comprehensive qualitative and quantitative investigation in various phases of TRIP steel microstructure. Therefore, a TRIP steel with chemical composition of 0.2C 1.43Si 1.5Mn was produced and its complicated microstructure which contained ferrite, bainite, martensite and retained austenite was investigated using X-Ray Diffractometry (XRD), optical microscopy (OM), field emission scanning microscopy (FE-SEM) and Electron backscatter diffraction (EBSD). The OM and FE-SEM results were used only to qualitative studies and identification of the morphologies of the phases but the EBSD results and functions were used to qualitative and quantitative studies. The volume fractions of retained austenite, ferrite涨꞊ and martensite phases were calculated and the amounts of 11%, 82% and 7% were obtained, respectively. The volume fraction of retained austenite was also measured with XRD and the amount of 14.3% was obtained.Keywords: TRIP steel, XRD, FE, SEM, EBSD, Retained austenite}
-
در این تحقیق پوشش های نانوساختار آهن-کبالت-تنگستن به روش آبکاری جریان مستقیم بر روی زیر لایه مسی حاصل شد. نتایج نشان داد که چگالی جریان پوشش دهی و نیز ترکیب شیمیایی محلول بر خواص مغناطیسی و ساختاری اثرگذار است. مورفولوژی پوشش های بدست آمده از دو حمام آبکاری متفاوت بوده و با افزایش چگالی جریان آبکاری مقدار فاز fcc موجود در ساختار دو فازی fcc+bcc کاهش یافت. مشاهده شد که پارامترهای آبکاری تاثیر چشمگیری بر روی تغییرات اندازه دانه نداشته و اندازه دانه پوشش ها کمتر از 20 نانومتر گزارش شد. با افزایش چگالی جریان، رسوب دهی تحت کنترل نفوذ درآمده و مقدار تنگستن رسوب کرده و در نتیجه میکروسختی پوشش ها کاهش یافت. با توجه به نتایج حاصل از پراش پرتو ایکس (XRD) و نیز مغناطش سنج نمونه لرزان (VSM)می توان تغییرات گسترده در مقدار وادارندگی را به تغییرات فازی در این پوشش ها مربوط دانست.کلید واژگان: خاصیت مغناطیسی, آبکاری الکتریکی, نانوساختار, آهن, کبالت, تنگستن}In this research, nanocrystalline FeCoW alloy coatings were electrodeposited on copper substrate. The results showed that current density and bath composition can affect structural and magnetic properties. However, surface morphology changed due to bath composition. Furthermore, by increasing current density, the amount of fcc phase decreased in fcc淇 double phase structure. It was observed that deposition parameters didnt change the grain size of the coatings efficiently, and this parameter was lower than 20 nm for all the cases. Due to the diffusional phenomenon that take places at higher current densities, the amount of deposited tungsten decreased, and thus lower microhardness values were reported. By comparing XRD and VSM data, it was assumed that the extensive change in the coercivity is related to the phase structure in these alloys.Keywords: Magnetic property, Electrodeposition, Nanostructure, Fe?Co?W}
-
در تحقیق حاضر آلیاژ های روکش سخت پایه Fe-Cr-C با نسبت (وزنی) متفاوت به روش SMAW به صورت تک لایه و دو لایه بر روی فولاد ساده کربنی ST 32 جوشکاری گردیدند. سپس نمونه هایی تهیه و آزمون های آنالیز شیمیایی (OES) ، متالوگرافی نوری،XRD، SEM، و خستگی حرارتی بر روی آنها انجام شد. نتایج آزمون پراش پرتو (XRD) X نشان داد که ریز ساختار لایه روکش سخت نمونه روکش سخت شده با الکترود( پر کربن –پر کروم) AB شامل کاربید اولیه و یوتکتیک و نمونه روکش سخت شده با الکترود (کم کربن –کم کروم)SD شامل آستنیت ومارتنزیت می باشد. تصاویر متالوگرافی نوری و الکترونی، آنالیز نقطه ای و نقشه توزیع عناصر نیز حضور فازهای فوق را تایید نموده است. نتایج آزمون خستگی حرارتی مشخص نمود در مجموع کلیه نمونه ها، بالاترین عمر خستگی حرارتی مربوط به نمونه روکش سخت شده با الکترود(کم کربن –کم کروم)SD قطر4 میلی متر در حالت تک لایه با کمترین (غلظت عنصر کروم) درصد حجمی آستنیت باقی مانده و کاربید (Cr،Fe)23C6 با ریز ساختار اولیه آستنیت، مارتنزیت و کاربید (Cr،Fe)23C6 می باشد، کمترین عمر خستگی حرارتی مربوط به نمونه روکش سخت شده با الکترود ( پر کربن –پر کروم) AB قطر 25/3 میلی متر در شرایط دو لایه با ریزساختار اولیه متشکل از کاربیدهای اولیه (Cr،Fe)7C3 و یوتکتیک می باشد.کلید واژگان: Fe, Cr, C, ریز ساختار, روکش سخت, خستگی حرارتی}In this Investigation two type of hard face coated electrodes (Fe-Cr-C) used as a hard facing alloys with different ratio Cr/C. The welding of hard facing electrodes were done in similar heat-input but in different of deposited layers on ST32 mild steel. The OES, OM, SEM and XRD techniques used for determining of chemical analysis and study of microstructure characteristics of hard face samples. In addition the thermal fatigue test were done at 600-25 OC for different samples and hardness test used for determining the hardness of hard face layers. The XRD examination Results indicated that microstructure of hard facing layer sample (AB electrode) includes primary carbides and eutectic (), the microstructure of hardfacing layer sample (SD electrode) includes austenite馪笢. The hardness result indicated that hardfacing samples (AB electrode) have maximum hardness which 52-58HRC and hard facing samples (SD electrode) with austenite martensite microstructure have minimum Hardness (30-50 HRC). The thermal fatigue Test results indicated, the highest fatigue life related to the sample that hard-faced with the SD electrode (Ø=4 mm) at a single layer and the lowest thermal fatigue life related to the sample that hard-faced with AB electrode (Ø=3.25 mm) at two layers. It was also found that there is an inverse relationship between hardness and thermal fatigue life of specimens.Keywords: Fe, Cr, C, Microstructure, Hard facing, Thermal Fatigue}
-
در این پژوهش تولید نانوپودر کامپوزیتی Co/ VC از مواد اولیه Co3O4، V2O5 و گرافیت با استفاده از پودر منیزیم به عنوان عامل احیا به روش مکانوشیمیایی بررسی شد. برای این منظور مخلوط پودری مواد طبق واکنش استوکیومتری در یک آسیا سیاره ای پرانرژی با نسبت وزنی پودر به گلوله 1:20 تحت آتمسفر گاز آرگون در زمان های مختلف آسیا شدند. پس از 10 دقیقه آسیاکاری احتراق صورت گرفته و با توجه به نتایج XRD، منیزیم توانسته اکسیدهای کبالت و وانادیم را احیا کرده و خود به اکسید منیزیم تبدیل شود و از طرفی گرافیت نیز با وانادیم فلزی، کاربید وانادیم تشکیل داده و واکنش به طور کامل انجام گرفته است. با توجه به دمای آدیاباتیک واکنش (3932.014Tad~)، این واکنش از نوع خود پیش رونده دما بالا یا MSR می باشد. اندازه بلورک های کاربید وانادیم و کبالت نیز از روش ویلیامسون- هال محاسبه گردید که به ترتیب 50 و 10 نانومتر گزارش شده است. در نهایت فاز اکسید منیزیم نیز توسط فرآیند اسیدشویی با اسید کلریدریک 9 درصد از سیستم حذف گردید و پودر کامپوزیتی Co/ VC تولید شد.
کلید واژگان: نانوکامپوزیت, مکانوشیمیایی, کاربید وانادیم, FE, SEM, MSR}In the present study, production of the composite nano powder of Co/VC by mechanochemical method from Co3O4, V2O5, and graphite as the starting materials with magnesium as the reduction agent was investigated. For this purpose, the materials powder mixture was milled in accordance with stoichiometric reaction in a high energy ball mill with the ball-to-powder ratio of 20:1 under argon atmosphere for different durations. After 10min of milling, combustion occurred and the XRD results indicated that magnesium has reduced vanadium and cobalt oxides (V2O5 and Co3O4) and has changed into magnesium oxide; also, graphite has reacted with the metallic vanadium to form vanadium carbide, which means that the reaction has been completed. Based on the adiabatic temperature of the reaction (Tad~ 3932.014), the reaction was identified as a mechanically inducted self-sustaining one or MSR. The crystallite sizes of vanadium carbide and cobalt calculated by the Williamson-Hall equation were 50 and 10nm, respectively. Finally, the magnesium oxide phase was deleted from the system via leaching process in 0.9% hydrochloric acid and the composite powder of Co/VC was obtained.Keywords: Nanocomposite, Mechanochemical, Vanadium carbide, FE, SEM, MSR} -
در این تحقیق، واکنش های بین ایلمنایت و آلومینیم به منظور تعیین اولین مرحله از واکنش های دستگاه ایلمنایت، آلومینیم و گرافیت با هدف تولید مواد مرکب Al2O3-TiC/Fe بررسی شده است. برای این منظور، ایلمنایت خالص تهیه شد. سپس، ایلمنایت و آلومینیم با نسبت مولی 1 به 2 مخلوط شدند و پس از فشرده شدن، در دماهای بحرانی به دست آمده از آزمون DTA عملیات حرارتی شدند. مشخص شد که ابتدا آلومینیم ذوب می شود و در ادامه، با ایلمنایت وارد واکنش می شود. در مراحل ابتدایی واکنش ایلمنایت و آلومینیم، آهن، تیتانیم و آلومینا تشکیل می شوند. با گذشت زمان، ذرات کروی Fe2Ti در ساختار زمینه ی آلومینا و تیتانیا ایجاد می شود.
کلید واژگان: ایلمنایت, آلومینیم, کامپوزیت هایFe, TiC, Al2O3}In this research، the first step of reactions in ilmenite-aluminum-graphite system for the formation of Al2O3-TiC/Fe composites was investigated by the study of the binary system of aluminum and ilmenite. The milled and pressed samples prepared by the synthesized ilmenite and aluminum powders having the molar ratio of 1:2 were heat treated at the critical temperatures obtained from DTA analysis. It was found that a transient Fe phase is formed along with TiO2. The spherical shaped Fe2Ti phase was then formed in the matrix consisting of TiO2 and Al2O3.
Keywords: Ilmenite, Aluminum, Fe, TiC, Al2O3 composites}
نکته
- نتایج بر اساس تاریخ انتشار مرتب شده‌اند.
- کلیدواژه مورد نظر شما تنها در فیلد کلیدواژگان مقالات جستجو شده‌است. به منظور حذف نتایج غیر مرتبط، جستجو تنها در مقالات مجلاتی انجام شده که با مجله ماخذ هم موضوع هستند.
- در صورتی که می‌خواهید جستجو را در همه موضوعات و با شرایط دیگر تکرار کنید به صفحه جستجوی پیشرفته مجلات مراجعه کنید.
©2000-2024 magiran.com All Rights Reserved.