جستجوی مقالات مرتبط با کلیدواژه "ecf" در نشریات گروه "صنایع چوب و کاغذ"

The objective of this research was accomplished on the effects of total chlorine free (TCF) and elemental chlorine free (ECF) bleaching on optical and mechanical properties of bagasse soda pulps. For this purpose, some unbleached bagasse soda pulps were randomly selected from Ahvaz Pars industry. Then these pulps were bleached with one, two and three P, OP, OPY, O(Ep)P, EHP and O(Ep)H bleaching stages by using oxygen(O) hydrogen peroxide(P), alkali extraction with hydrogen peroxide(Ep), sodium hypochlorite(H) and sodium dithionite(Y). The hand sheets with 70 gr/m2 were prepared from above-mentioned of pulps, and then the optical and mechanical properties were measured and compared according by using TAPPI standard test methods. The results showed that brightness, greenness, tear (except EHP stages), tensile, burst, breaking length strengths and folds were increased and opacity and a* factor were decreased by ECF and TCF bleaching stages. The effects of TCF bleaching stages were more sensible than ECF bleaching stages in improve of bagasse soda properties, too. In general, role of three OPY and O(Ep)H stages and two OP bleaching stages were better than EH(control) stage and unbleached bagasse soda pulps mill in improve of brightness and its paper strengths, too.

A fundamental study was carried out to explore the canola stalks properties in order to increase the use of abundant agricultural residuals in pulp and paper production. In this study, the morphological, chemical composition and soda pulping properties of Canola stalks were investigated. The results showed that except the thicker cell wall, the morphological properties of Canola stalks fibers were comparable to those of nonwoods and hardwoods fibers. Chemical analysis indicated that Canola stalks contains lower amount of cellulose (44%), while the lignin, hemicelluloses and ash content of Canola stalks are comparable to other non-woods. In comparison with most of non wood fiber resources, soda pulping of Canola stalks required higher chemical charge and pulping time. Soda pulping of Canola stalks in 22% active alkaline and 100 min in max temperature produced pulp with 82.6% ISO of brightness The strength properties of bleached Canola stalks soda pulp include tensile index (Nm/g), burst index (kpam2/g) & tear index (mNm2/g) showed respectively 63.6, 2.22 & 4.9.