Investigation on utilization The mechanical of Fish wastes (WF) in manufacturing of biodegradable wood plastic composites (WPCs) and high density polyethylene (HDPE)

In this study, the effect of fish waste powder, base material polyethylene, and also the quantity of coupling agent (MAPE) on physical and mechanical properties of wood-plastic composite were studied. For this purpose, wood powder at 40% was mixed with 60% of HDPE. Fish waste in three levels (5, 10 and 15%) mixed into wood powder and coupling agent on three levels (0, 2 and 4) of HDPE in a blender at 180 °C and a speed rotating of 50 rpm, and samples were made with using of injection molding for standard tests. The mechanical properties: tensile and bending strength, bending and tensile modulus were investigated according of ASTM standards. This result suggests that increasing the amount of fish powder waste to 10%, increased bending strength while other strengths diminished. The amounts of all strengths were increased by increasing in percentage of coupling agent to 4%.The results shows that fish waste was suitable as a new material for wood plastics composites.