Effect of Annealing Temperature and Composition on Magnetic Properties of Manganese-Bismuth Homogenized in Tube Furnace
Repeated heat treatment on manganese-bismuth (MnBi) in a tube furnace increases the homogeneity of rare-earth-free magnets. Ferromagnetic low temperature phase (LTP) MnBi is formed after heating Mn and Bi in a ratio of 2:1 at 1000 °C for 1 h and then 400 °C for 1 h. Areas with comparable compositions of Mn and Bi are detected, but some Mn and Bi remains segregate after using this stepped heating 3 times. The subsequent annealing at 340 °C gives rise to higher magnetizations and coercivity than those using 410 °C annealing. Increasing the starting Mn:Bi ratio to 4:1 reduces the coercivity and remanent magnetization due to the increase in Mn oxidation at the expense of ferromagnetic phase.
پرداخت حق اشتراک به معنای پذیرش "شرایط خدمات" پایگاه مگیران از سوی شماست.
اگر عضو مگیران هستید:
اگر مقاله ای از شما در مگیران نمایه شده، برای استفاده از اعتبار اهدایی سامانه نویسندگان با ایمیل منتشرشده ثبت نام کنید. ثبت نام
- حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران میشود.
- پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانههای چاپی و دیجیتال را به کاربر نمیدهد.