Cation Distribution of Co-Ni-Mn Ferrites from Magnetization and Magnetostriction

Message:
Article Type:
Research/Original Article (دارای رتبه معتبر)
Abstract:

Nickel doped CoMn ferrites with high magnetization were synthesized by double sintering solid state route with compositions of Co0.7-xNixMn0.3Fe2O4 with x = 0, 0.05, 0.1 and 0.15. Theoretical Cation distribution for cubic spinel ferrites was suggested on basis of electrical configuration expectations and cation site preferences. Cation distribution suggested was in good agreement with experimental results obtained from VSM and XRD. Values of theoretically calculated magnetic moment, coercivity and magnetization are in good agreement with experimental data obtained from VSM. Maximum saturation magnetization of 37.7emu/gm is obtained for sample Co0.7Mn0.3Fe2O4 at magnetic field of 5K Oe. Magnetostriction was found to increase with increasing magnetic field (from 1KOe to 5KOe.) Maximum magnetostriction of 84ppm was observed for sample Co0.7Mn0.3Fe2O4 at 5KOe. Maximum magnetization of magnetoelectric composites with 30% Co0.7-xNixMn0.3Fe2O4 – 70% PbZr0.48Ti0.52 was found to be 7.4 emu/g for composition with x = 0.

Language:
English
Published:
Iranian Journal of Materials science and Engineering, Volume:21 Issue: 1, Mar 2024
Page:
9
https://magiran.com/p2703436  
دانلود و مطالعه متن این مقاله با یکی از روشهای زیر امکان پذیر است:
اشتراک شخصی
با عضویت و پرداخت آنلاین حق اشتراک یک‌ساله به مبلغ 1,390,000ريال می‌توانید 70 عنوان مطلب دانلود کنید!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی نامحدود همه کاربران به متن مطالب تهیه نمایند!
توجه!
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.
In order to view content subscription is required

Personal subscription
Subscribe magiran.com for 70 € euros via PayPal and download 70 articles during a year.
Organization subscription
Please contact us to subscribe your university or library for unlimited access!