Determination of Mechanical Characteristics of Types of Fiber concrete at High Temperatures

Concrete is the most used construction material in the world. Today, there are various concretes with different applications in the industry. One of the types of concrete is fiber concrete. In this study, several concrete samples were made with steel, glass and polypropylene fibers and the effect of the volume and weight percentages of each of the fibers in improving the compressive strength of the samples at temperatures Different has been checked. In order to check the results and the possibility of comparing it with the behavior of normal concrete, a type of concrete without fibers was also made using common materials and similar tests were performed on it. Based on the investigations, the results showed that the concrete samples with steel fibers tolerated higher temperature levels and had higher resistance compared to other samples. In the samples, by adding 0.25% and 0.5% by volume of steel fibers to concrete, respectively, the compressive strength of the sample at high temperatures was improved. The strength of concrete samples with 3400 Kg/m was slightly decreased by increasing the percentage of fibers from 0.5% to 0.75%. The compressive strength of concrete containing steel fibers is 20% higher than that of concrete containing propylene fibers.