اثر اکسید بیسموت بر فاکتور کیفیت, دمای کوری و میزان انقباض فریت منگنز - روی
نویسنده:
چکیده:
Bi2O3 was added to the Mn-Zn ferrite (52 mol % Fe2O3, 34 mol% MnO, 14 mol% ZnO) in the amounts of 0.03, 0.08, 0.2, 1 and 5 wt%. Q factor, Curie temperature and linear shrinkage were investigated. Several sintering conditions were practiced. The optimum sintering condition (1200 °C for 1 hour) was determined based on the maximum value of the Q factor of undoped ferrite. The net magnetic moment, Curie point and shrinkage behavior of the material were influenced by Bi2O3. Results showed that in small additions of Bi2O3 (0.03 wt %), the Q factor was the maximum, and with increasing Bi2O3, the linear shrinkage decreased. The Curie temperature changed in two stages; it increased in the first where Bi2O3 was below 1 wt%, and then decreased above this value.
کلیدواژگان:
Mn ، Zn ferrite ، Bi2O3 ، Curie temperature ، Q factor ، linear shrinkage
زبان:
انگلیسی
صفحات:
441 تا 445
لینک کوتاه:
magiran.com/p441982
دانلود و مطالعه متن این مقاله با یکی از روشهای زیر امکان پذیر است:
اشتراک شخصی
با عضویت و پرداخت آنلاین حق اشتراک یکساله به مبلغ 1,390,000ريال میتوانید 70 عنوان مطلب دانلود کنید!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی نامحدود همه کاربران به متن مطالب تهیه نمایند!
توجه!
- حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران میشود.
- پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانههای چاپی و دیجیتال را به کاربر نمیدهد.
In order to view content subscription is required
Personal subscription
Subscribe magiran.com for 70 € euros via PayPal and download 70 articles during a year.
Organization subscription
Please contact us to subscribe your university or library for unlimited access!