Degradation and cyclic crack resistance of continuous casting machine roll material under operating temperatures

Author(s):

P. Maruschak , D. Baran

Message:
Abstract:
The in-service cracks of the continuous casting machine roll are studied. The effects of high temperature fatigue crack growth were investigated for 25Kh1M1F steel, which is widely used for continuous casting rolls. In general, fatigue crack growth rates increased with increasing temperatures. At high crack growth rates, crack-tip plasticity was significant and propagation proceeded by ductile striation formation processes.
Language:
English
Published:
Iranian Journal of science and Technology (B: Engineering), Volume:35 Issue: 5, August 2011
Pages:
159 to 165
https://magiran.com/p926972  
دانلود و مطالعه متن این مقاله با یکی از روشهای زیر امکان پذیر است:
اشتراک شخصی
با عضویت و پرداخت آنلاین حق اشتراک یک‌ساله به مبلغ 1,390,000ريال می‌توانید 70 عنوان مطلب دانلود کنید!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی نامحدود همه کاربران به متن مطالب تهیه نمایند!
اطلاعات بیشتر
توجه!
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.
In order to view content subscription is required

Personal subscription
Subscribe magiran.com for 70 € euros via PayPal and download 70 articles during a year.
Organization subscription
Please contact us to subscribe your university or library for unlimited access!
More information