The article discusses the effect of calcined clays on the properties of Portland cement. An optimal method for calcining clays is proposed, which makes it possible to reduce the proportion of Portland cement clinker in cement to 60% and increase the strength characteristics from 55 MPa to 79 MPa. The study of the composition and structure of clays made it possible to select the optimal heat treatment parameters, at which the calcination products are characterized by the highest pozzolanic activity. It is shown that the use of alkali-activated calcined clays significantly increases the strength and durability of hardened cement binders compared to the composition without additives. In addition, calcined clays increase the frost resistance of cement in a 5% NaCl solution. The obtained experimental data are confirmed by thermodynamic calculations and the results of scanning electron microscopy.

The construction sector is responsible for relevant environmental impacts and one of its most crucial points is the use of concrete. Geopolymers represent the most promising green and ecological alternative for common Portland cement and cementitious materials, due to its proven durability, mechanical and thermal properties. This work presents an experimental and comparative study of adhesion at the fiber-matrix interface between glass fibers and carbon fibers added to the geopolymer matrix. This analysis was performed by pull-out test, whereby it was found that the greatest efficiency was obtained by reinforcing with the glass fibers, incorporated at 2 mm in the geopolymer matrix. As results, the adhesion between the fibers and the geopolymer structure can be assessed, as well as the optimum length of application.